Cemix Products Ltd logo

repairs & grouts





  • 20KG



CEMIX STRUCTURAL REPAIR VO is a high-performance fibre reinforced, polymer and micro silica modified, shrinkage compensated, concrete repair mortar for concrete repairs & patching in 5mm + vertical & overhead applications. It is typically hand placed but can also be wet sprayed onto concrete substrates. It is used in remedial works where high performance & durability are required.



  • Vertical & overhead repairs to concrete structures
  • Columns
  • Underside of beams & slabs
  • Bridges
  • Marine structures
  • Water retaining structures
  • Precast concrete
  • Sewage and water treatment tanks
  • Man holes


  • One component
  • Versatile 5mm to high-build application depths
  • Vertical, overhead & horizontal use
  • Hand placed or wet sprayed
  • Fibre reinforced
  • Shrinkage compensated
  • Short curing times
  • High bond strength
  • Durable
  • Waterproof
  • Impermeable to water borne aggressors such as chloride ions
  • Improved abrasion resistance
  • Polymer modified
DURABILITY ENHANCER, STEEL PROTECTION & WATERPROOFING CEMIX STRUCTURAL REPAIR VO contains an integral crystalline concrete durability enhancer & waterproofing material, which further protects & waterproofs the mortar in-depth by making it completely impermeable to water borne aggressors such as chloride ions. This admixture permanently protects the mortar & imbedded structural steel from long-term corrosion & deterioration. SUBSTRATE PREPARATION Concrete substrates should be sound & roughened to ensure a good bond. They should be uncoated & clean, free from all contaminants, loose particles, dirt, oil, mould, curing compounds, sealers & paints etc. For a durable repair cut a square or rectangular perimeter edge around the repair at least 10mm in depth. Remove all oxidation from exposed rebar & ensure that there is at least 25mm (or ‘finger room’) behind each rebar. For deep critical repairs use anchors and steel mesh as required to enhance bonding. The better the substrate preparation & condition the better the end result. The concrete substrate should ideally be at least 3 months old. MOVEMENT / CONTROL JOINTS Honour any control joints in the concrete substrate – do not apply product over control joints. MIXING Mix whole bags of product. Add 2.7L of water to mixer & then add product gradually to water. Add rest of water slowly whilst mixing until the desired consistency is achieved. Maximum total water is approximately 3.2L per 20kg bag. Mix thoroughly for 4 minutes using a drill & paddle or mechanical mortar mixer. Do not mix more product than can be mixed, placed & finished in 45 minutes. In hot weather consider using chilled mixing water. In very cold weather consider using warm mixing water. APPLICATION Dampen the concrete substrate and then thoroughly prime it with Cemix®Multibond brushed undiluted into the surface just prior to mortar application. Firmly push the CEMIX STRUCTURAL REPAIR VO into the surface to obtain a wet bond while the CEMIX MULTIBOND is still wet. Do not let the CEMIX MULTIBOND dry. Application is from one side of the repair to the other completely filling the void. Firmly compact the mortar into the void & trowel finish as required. CEMIX STRUCTURAL REPAIR VO can be used from 5mm depths upwards, however for a durable repair in demanding applications, apply product to a minimum depth of 10mm. Fill void to a maximum depth of 30mm for overhead applications & 40mm for vertical applications in one go. Apply product in layers for thicker repairs - Roughen the preceding layer prior to it hardening & prime the preceding layer after it has hardened as discussed above. Depending on the situation, repairs up to 100mm can be achieved in layers of wet on wet. CURING It is very important to prevent early plastic state moisture loss prior to the product setting. Cure product thoroughly after it has set by keeping it wet & covered for at least 7 days. Avoid product freezing for at last 3 days. TECHNICAL DATA
  • Appearance – Sand/Cement grey powder.
  • Strength (MPa) - 30MPa @ 7 days; 50MPa @ 28 days
  • Application Temp- 5ºC to 30ºC
  • Yield / Coverage - Approximately 11.1L or 0.0111m3 per 20kg bag.
  • Bond Strength – > 3MPa
  • Thermal Coeff. Of Exp – 9.0 x 10-6 mm/mm/ ºC
  • Chloride Ion Permeability – < 1000 coulombs
  • Working Time – 30 minutes at 20ºC
The data shown above reflects typical results based on laboratory testing under controlled conditions. Reasonable variations may occur on site. LIMITATIONS Substrate Temperature - +5°C min. / +30°C max. Ambient Temperature - +5°C min. / +30°C max. CLEANING Clean all tools with water & brush immediately after use. STORAGE Can be stored in its original packaging in a dry place well sealed for a period of six (6) months after production. Do not store opened bags.